Lexan EXL1413T 嘉博塑化有限公司专业销Lexan EXL1413T沙伯根本立异塑料PC原厂原包江浙沪一级代办署理 质量包管.品种齐备.诚信经营.老少无欺.接待来电咨询订购 原厂原包Lexan EXL1413T沙伯根本立异塑料江浙沪一级代办署理/PC简介 LEXAN由双酚A制造,为聚碳酸脂这高份子材料,具有**的高透明和耐热温度,和热可塑性树脂中的冲击强度,杰出的成型性使得“LEXAN”用在汽车零组件、事务机械、家电产物、电子产物、电子零件、食物用具、医疗器材和通讯装备之替换金属用品上,的选择材料。 产物描写 Lexan PC EXL1413T物性表 “Lexan EXL1413T resin是一种聚碳酸酯产物,它可以经由过程打针成型进行加工。 特征包罗: 阻燃/额定火焰 共聚物 加工机能杰出 快速成型周期 柔嫩”。 Property/特征 Lexan* EXL1413T polycarbonate siloxane copolymer resin is a transparent injection molding grade. This resin offers excellent low temperature ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. Lexan EXL1413T resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications. MECHANICAL/机械机能 Tensile Stress, yld, Type I / 抗张水平,屈就,类型I, 50 mm/min 58 MPa ASTM D 638 Tensile Stress, brk, Type I / 抗张水平,断裂,类型I, 50 mm/min 64 MPa ASTM D 638 Tensile Strain, yld, Type I / 拉伸伸长,屈就,类型I, 50 mm/min 5.8 % ASTM D 638 Tensile Strain, brk, Type I / 拉伸伸长,断裂,类型I, 50 mm/min 131.4 % ASTM D 638 Tensile Modulus / 拉伸模量, 50 mm/min 2210 MPa ASTM D 638 Flexural Stress, yld / 挠曲强度, 屈就 , 1.3 mm/min, 50 mm span 94 MPa ASTM D 790 Flexural Modulus / 挠曲模量, 1.3 mm/min, 50 mm span 2210 MPa ASTM D 790 Tensile Stress, yield / 抗张水平,屈就, 50 mm/min 57 MPa ISO 527 Tensile Stress, break / 抗张水平,断裂, 50 mm/min 61 MPa ISO 527 Tensile Strain, yield / 拉伸伸长,屈就, 50 mm/min 5.5 % ISO 527 Tensile Strain, break / 拉伸伸长,断裂, 50 mm/min 124.9 % ISO 527 Tensile Modulus / 拉伸模量, 1 mm/min 2350 MPa ISO 527 Flexural Stress, yield / 曲折强度,屈就, 2 mm/min 90 MPa ISO 178 Flexural Modulus / 挠曲模量, 2 mm/min 2150 MPa ISO 178 Hardness,Rockwell / 洛氏硬度 L 89 – ISO 2039-2 IMPACT/冲击机能 Izod Impact, notched / 悬臂梁缺口冲击强度, 23°C 890 J/m ASTM D 256 Izod Impact, notched / 悬臂梁缺口冲击强度, -30°C 795 J/m ASTM D 256 Instrumented IMPACT Total Energy / 装有丈量仪表的落镖冲击总能量, 23°C 82 J ASTM D 3763 Instrumented IMPACT Total Energy / 装有丈量仪表的落镖冲击总能量, -30°C 85 J ASTM D 3763 Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*3 23°C NB kJ/m² ISO 180/1U Izod Impact, unnotched / 无缺口悬臂梁冲击 80*10*3 -30°C NB kJ/m² ISO 180/1U Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*3 23°C 65 kJ/m² ISO 180/1A Izod Impact, notched / 悬臂梁缺口冲击强度 80*10*3 -30°C 55 kJ/m² ISO 180/1A Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm 70 kJ/m² ISO 179/1eA Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm 60 kJ/m² ISO 179/1eA Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm NB kJ/m² ISO 179/1eU THERMAL/热机能 Vicat Softening Temp, Rate / 维卡软化温度,品级 A/50 141 °C ASTM D 1525 HDT, 1.82 MPa, 3.2mm, unannealed 124 °C ASTM D 648 CTE, -40°C to 95°C, flow 7.15E-05 1/°C ASTM E 831 CTE, -40°C to 95°C, xflow 7.93E-05 1/°C ASTM E 831 CTE, 23°C to 80°C, flow 7.15E-05 1/°C ISO 11359-2 CTE, 23°C to 80°C, xflow 7.93E-05 1/°C ISO 11359-2 Ball Pressure Test, 125°C /- 2°C pass – IEC 60695-10-2 Vicat Softening Temp, Rate / 维卡软化温度,品级 B/50 141 °C ISO 306 Vicat Softening Temp, Rate / 维卡软化温度,品级 B/120 142 °C ISO 306 HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm 118 °C ISO 75/Af Relative Temp Index, Elec / 相对热指数, 电机能 130 °C UL 746B Relative Temp Index, Mech w/o impact / 相对热指数,非机械冲击机能 130 °C UL 746B PHYSICAL/物理机能 Specific Gravity / 比重 1.19 – ASTM D 792 Mold Shrinkage / 缩短率, flow, 3.2 mm 0.4 – 0.8 % SABIC Method Mold Shrinkage / 缩短率, xflow, 3.2 mm 0.4 – 0.8 % SABIC Method Melt Flow Rate / 熔流率 300°C/1.2 kgf 10 g/10 min ASTM D 1238 Density / 密度 1.19 g/cm³ ISO 1183 Water Absorption / 吸水率, 0.12 % ISO 62 Moisture Abso�����app.txtrption / 吸水率, 均衡 0.09 % ISO 62 Melt Volume Rate / 熔解体积流率, MVR at 300°C/1.2 kg 9 cm³/10 min ISO 1133 OPTICAL/光学机能 Light Transmission / 透光率 82 % ASTM D 1003 Haze / 雾度 3 % ASTM D 1003 ELECTRICAL/电气机能 Volume Resistivity / 体积电阻率 1.E 15 Ohm-cm ASTM D 257 Surface Resistivity / 概况电阻率 1.E 15 Ohm ASTM D 257 FLAME CHARACTERISTICS/火焰特征 UL Recognized, 94V-2 Flame Class Rating / 阻燃品级 2.5 mm UL 94 Glow Wire Flammability Index / 炽热丝易燃指数 960°C, passes at 3 mm IEC 60695-2-12 Glow Wire Ignitability Temperature / 热灯丝焚烧温度, 0.8 mm 825 °C IEC 60695-2-13 Glow Wire Ignitability Temperature / 热灯丝焚烧温度, 3.0 mm 825 °C IEC 60695-2-13